Tubo de acero sin soldadura recocido recocido para caldera
|
Product Name
|
ASTM A213 316Ti stainless steel seamless tube
|
|
Material
|
stainless steel 316Ti
|
|
Process
|
cold drawn, cold rolling
|
|
Standard
|
A213, A312, A269, A511
|
|
Grade
|
304, 304L, 316L, 321, 347H, S31803, 904L
|
|
Size
|
6 - 610 mm
|
|
Length
|
800mm - 20000 mm
|
|
Used
|
bolier, heat exchanger
|
Tolerancia para tubos de caldera inoxidables sin costura:
|
Production Method
|
Size(mm)
|
Tolerance
|
|
Hot Rolling(Extrusion)
|
OD
|
≤140
|
±1.25%
|
|
＞140
|
±1.0%
|
|
WT
|
≤10
|
±12.5%
|
|
＞10
|
±15%
|
|
Cold Drawn(Cold Rolled)
|
OD
|
8~30
|
±0.20mm
|
|
＞30~50
|
±0.30mm
|
|
＞50
|
±0.8%
|
|
WT
|
1.0~3
|
+12%
-10%
|
|
＞3.0
|
±10%
|
|
Standard
|
ASME SA213/ASTM A213, ASTM A269/ASME SA269, ASME SA312/ASTM A312, ASME249/ASTM A249, ASME SA511/ASTM A511, ASTM A270/ASME SA270, EN10216-5,EN10305-1, EN10217-5, DIN 17175, DIN 2448, DIN 6258, GOST 8731, JIS G3463, JIS G3462, JIS G3455, JIS G3459 etc.
|
|
Material
|
TP304, TP304L, TP304H, TP304LN, TP314, TP316, TP316L, TP316LN, TP321, TP321H, TP310, TP310S, TP317, TP317L, TP347, TP347H, N08904, 904l, 253MA(S30815), 254SMO(S31254).
|
|
Type
|
Seamless / SML
|
|
O.D
|
6-530mm
|
|
W.T
|
0.7-50mm
|
|
Length
|
0-38000mm
|
|
Technique
|
Cold Finished (Cold Drawing and Cold Rolling), Hot Finished (Hot Extrusion)
|
|
Ends
|
PE/Plain Ends, BE/Beveled Ends
|
Composición
Gamas de composición para acero inoxidable grado 316 .
|
Grade
|
|
C
|
Mn
|
Si
|
P
|
S
|
Cr
|
Mo
|
Ni
|
N
|
|
316
|
Min
|
-
|
-
|
-
|
0
|
-
|
16.0
|
2.00
|
10.0
|
-
|
|
Max
|
0.08
|
2.0
|
0.75
|
0.045
|
0.03
|
18.0
|
3.00
|
14.0
|
0.10
|
|
316L
|
Min
|
-
|
-
|
-
|
-
|
-
|
16.0
|
2.00
|
10.0
|
-
|
|
Max
|
0.03
|
2.0
|
0.75
|
0.045
|
0.03
|
18.0
|
3.00
|
14.0
|
0.10
|
|
316H
|
Min
|
0.04
|
0.04
|
0
|
-
|
-
|
16.0
|
2.00
|
10.0
|
-
|
|
max
|
0.10
|
0.10
|
0.75
|
0.045
|
0.03
|
18.0
|
3.00
|
14.0
|
-
|
Propiedades mecánicas
Propiedades mecánicas del acero inoxidable grado 316.
|
Grade
|
Tensile Str (MPa) min
|
Yield Str 0.2% Proof (MPa) min
|
Elong (% in 50 mm) min
|
Hardness
|
|
Rockwell B (HR B) max
|
Brinell (HB) max
|
|
316
|
515
|
205
|
40
|
95
|
217
|
|
316L
|
485
|
170
|
40
|
95
|
217
|
|
316H
|
515
|
205
|
40
|
95
|
217
|
Propiedades físicas
Propiedades físicas típicas del acero inoxidable de grado 316 .
|
Grade
|
Density(kg/m3)
|
Elastic Modulus (GPa)
|
Mean Co-eff of Thermal Expansion (µm/m/°C)
|
Thermal Conductivity (W/m.K)
|
Specific Heat 0-100 °C (J/kg.K)
|
Elec Resistivity (nΩ.m)
|
|
0-100 °C
|
0-315 °C
|
0-538 °C
|
At 100 °C
|
At 500 °C
|
|
316/L/H
|
8000
|
193
|
15.9
|
16.2
|
17.5
|
16.3
|
21.5
|
500
|
740
|
Comparación de especificación de grado
Especificaciones de grado para acero inoxidable de grado 316 .
|
Grade
|
UNS No
|
Old British
|
Euronorm
|
Swedish SS
|
Japanese JIS
|
|
BS
|
En
|
No
|
Name
|
|
316
|
S31600
|
316S31
|
58H, 58J
|
1.4401
|
X5CrNiMo17-12-2
|
2347
|
SUS 316
|
|
316L
|
S31603
|
316S11
|
-
|
1.4404
|
X2CrNiMo17-12-2
|
2348
|
SUS 316L
|
|
316H
|
S31609
|
316S51
|
-
|
-
|
-
|
Propiedad mecanica
El tratamiento térmico de las propiedades mecánicas longitudinales de las tuberías de acero se ajustará a la norma.
|
Material
|
Tensile strength MPa
≥
|
Yield Strength MPa
≥
|
Elongation
%
≥
|
|
0Cr18Ni9
|
520
|
205
|
35
|
|
1Cr19Ni9
|
520
|
205
|
35
|
|
0Cr19Ni10
|
480
|
175
|
35
|
|
1Cr18Ni9Ti
|
550
|
205
|
40
|
|
0Cr18Ni12Mo2Ti
|
530
|
205
|
35
|
|
0Cr26Ni5Mo2
|
590
|
390
|
18
|
|
1Cr17
|
410
|
245
|
20
|
|
00Cr27Mo
|
410
|
245
|
20
|
|
1Cr25Ti
|
440
|
245
|
17
|
Dureza:
Para los tubos que WT ≥2 mm, se deben realizar pruebas de dureza Rockwell.
Pruebas de los tubos de caldera sin soldadura:
Prueba 1.Bending:
Los tubos deben realizar la prueba de flexión cuando OD ≤22mm. El ángulo de flexión es de 90 grados, y el radio de flexión es 6 veces el diámetro exterior del tubo de acero.
2. Prueba hidráulica;
Pruebas de corrientes de Foucault, se pueden usar pruebas ultrasónicas en lugar de pruebas hidráulicas. Cuando las pruebas de corrientes de Foucault, GB / T 7735-1995 Gr. A debe seguirse; cuando las pruebas de ultrasonidos, GB / T 5777-1996 Gr. C8 debe ser seguido.
3. Prueba de aplanamiento.
4. Flanging prueba
5. Expandir la prueba